Description
The coated liquid silicone rubber is composed of three products, IOTA-2271 is the surface layer, with excellent release effect; IOTA-2440-1 is the intermediate layer, providing better strength and flexibility for the product; IOTA-2430-1 is the bottom layer, which has a certain adhesion with the cloth.
Technical index:
Item
|
IOTA-2271
|
IOTA-2440-1
|
IOTA-2430-1
|
Appearance
|
Transparent
|
White
|
Translucent
|
Viscosity (mPa.s)
|
50000
|
45000
|
50000
|
Density(g/cm³)
|
1.04
|
1.14
|
1.09
|
Hardness(ShoreA)
|
70
|
43
|
30
|
Tensile strength (MPa)
|
8.0
|
5.0
|
4.5
|
Elongation (%)
|
100
|
260
|
430
|
Tear strength (KN/m)
|
15
|
13
|
9.8
|
Note: 1. Curing condition: first vulcanization at 130 ℃ for 5 minutes.
2. The above data are for reference only.
Advantages:
Good release
High strength
Good liquidity
Application:
Coating release
Glasses nose holder
Crafts
Usage
1) Mixing ratio: 1:1 weight mixing and remove the air bubble.
2) Curing Condition: coated liquid silicone rubber under high temperature, it will cure quickly. The curing time depends on the thickness and curing temperature used.
3) Operation time:After mixing components A and B, the validity period of the mixture at 25 ° C is 48 hours.
Clean
Most hydrocarbon solvents can remove uncured silicon. Polar solvents, such as ketone and ethanol, cannot be removed.
Packing and storage
1) Package: 20kg / barrel, 200kg /Iron barrel.
2) Store at room temperature under 32°C to avoid exposure to rain and sunlight.
3) Shelf life:9 months, preferably within 6 months.